Corrosion resistance is
chosen with stainless steel of the austenite organization including
Cr 13-30% and Ni 6-20% and the Cr system is chosen. |
High frequency
sign |
JIS
sign |
Chemical
composition(%) |
Character
and usage |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Cu |
Others |
U201 |
SUS201 |
0.15
or less |
1.00
or less |
5.50`
7.50 |
0.060
or less |
0.0
under-30 |
3.50`
5.50 |
16.00`
18.00 |
- |
- |
N
0.25
or less |
Ni
saving steel kind and 301 substitution steels. It has magnetism
by the cold working. Rolling stock. |
U202 |
SUS202 |
0.15
or less |
1.00
or less |
7.50`
10.00 |
0.060
or less |
0.0
under-30 |
4.00`
6.00 |
17.00`
19.00 |
- |
- |
N
0.25
or less |
Ni
saving steel kind and 302 substitution steels. Cooking utensils.
|
U301 |
SUS301 |
0.15
or less |
1.00
or less |
2.00
or less |
0.045
or less |
0.0
under-30 |
6.00`
8.00 |
16.00`
18.00 |
- |
- |
- |
The
high intensity is obtained by the cold working. Rolling stock, belt
conveyor, bolt, nut, and spring. |
U302 |
SUS302 |
0.15
or less |
1.00
or less |
2.00
or less |
0.045
or less |
0.0
under-30 |
8.00`
10.00 |
17.00`
19.00 |
- |
- |
- |
The
expansion is a little inferior to 301 though the high intensity
is obtained by the cold working. Building exterior material. |
U303 |
SUS303 |
0.15
or less |
1.00
or less |
2.00
or less |
0.20
or less |
0.15
more |
8.00`
10.00 |
17.00`
19.00 |
|
- |
- |
On
inclination of ..being ground.. printing. It is the best for an
automatic board. Bolt and nut. |
U303Se |
SUS303Se |
0.15
or less |
1.00
or less |
2.00
or less |
0.20
or less |
0.060
or less |
8.00`
10.00 |
17.00`
19.00 |
- |
- |
Se
0.15
more |
On
inclination of ..being ground.. printing. It is the best for an
automatic board. Rivet and screw. |
U304 |
SUS304 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
8.00`
10.50 |
18.00`
20.00 |
- |
- |
- |
It
most widely uses it as stainless steel and heat resisting steel.
For food equipment, generalization study equipment, and nuclear
power |
U304L |
SUS304L |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
9.00`
13.00 |
18.00`
20.00 |
- |
- |
- |
304
extra-low carbon steels. Parts in which cannot it excel in intergranular
corrosion, and post weld heat treatment be done. |
U304N1 |
SUS304N1 |
0.08
or less |
1.00
or less |
2.50
or less |
0.040
or less |
0.0
under-30 |
7.00`
10.50 |
18.00`
20.00 |
- |
- |
N
0.10`
0.25 |
N
is added to 304, strength is improved while suppressing the decrease
of ductility, and there is thickness reducing effectiveness of the
raw material. Strength member for structure. |
U304N2 |
SUS304N2 |
0.08
or less |
1.00
or less |
2.50
or less |
0.040
or less |
0.0
under-30 |
7.50`
10.50 |
18.00`
20.00 |
- |
Nb
0.15
or less |
N
0.15`
0.30 |
N
and Nb were added to 304, and the effect of the ditto was given.
The usage is the same as 304N1 |
U304LN |
SUS304LN |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
8.50`
11.50 |
17.00`
19.00 |
- |
- |
N
0.12`
0.22 |
N
was added to 304L, and the effect of the ditto was given. It excels
in intergranular corrosion though the usage applies to 304N1. |
U305 |
SUS305 |
0.12
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
10.50`
13.00 |
17.00`
19.00 |
- |
- |
- |
Work
hardening is lower than 304. For cold forging ..pulling out specially...
the spatula stop |
U309S |
SUS309S |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
13.00`
15.00 |
22.00`
24.00 |
- |
- |
- |
It
is often actually used as heat resisting steel though corrosion
resistance is more excellent than 304. |
U310S |
SUS310S |
0.08
or less |
1.50
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
19.00`
22.00 |
24.00`
26.00 |
- |
- |
- |
An
oxidizing is excellent by 309 left-hand lays, and it is used actually
as heat resisting steel. |
U316 |
SUS316 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
10.00`
14.00 |
16.00`
18.00 |
2.00`
3.00 |
- |
- |
There
is corrosion resistance that is more excellent than 304 in various
media including seawater. Pitting corrosion raw material. |
U316L |
SUS316L |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
12.00`
15.00 |
16.00`
18.00 |
2.00`
3.00 |
- |
- |
316
extra-low carbon steels. The one that intergranular corrosion was
given to character of 316. |
U316N |
SUS316N |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
10.00`
14.00 |
16.00`
18.00 |
2.00`
3.00 |
- |
N
0.10`
0.22 |
N
is added to 316, strength is improved while suppressing the decrease
of ductility, and there is thickness reducing effectiveness of the
raw material. Strength member with excellent corrosion resistance.
|
U316LN |
SUS316LN |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
10.50`
14.50 |
16.50`
18.50 |
2.00`
3.00 |
- |
N
0.12`
0.22 |
N
was added to 316L, and the characteristic of the ditto was given.
It excels in intergranular corrosion though the usage applies to
316N. |
U316J1 |
SUS316J1 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
10.00`
14.00 |
17.00`
19.00 |
1.20`
2.75 |
1.00`
2.50 |
- |
Raw
material for sulfuric acid whose corrosion resistance and pitting
corrosion are more excellent than 316. |
U316J1L |
SUS316J1L |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
12.00`
16.00 |
17.00`
19.00 |
1.20`
2.75 |
1.00`
2.50 |
- |
Low
carbon steel of 316J1. The one that intergranular corrosion was
given to 316J1. |
U317 |
SUS317 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
11.00`
15.00 |
18.00`
20.00 |
3.00`
4.00 |
- |
- |
A
pitting corrosion is more excellent than 316. Dye equipment raw
material etc. |
U317L |
SUS317L |
0.030
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
11.00`
15.00 |
18.00`
20.00 |
3.00`
4.00 |
- |
- |
317
extra-low carbon steels. The one that intergranular corrosion was
given to 317. |
U317J1 |
SUS317J1 |
0.040
or less |
1.00
or less |
2.50
or less |
0.040
or less |
0.0
under-30 |
15.00`
17.00 |
16.00`
19.00 |
4.00`
6.00 |
- |
- |
For
environment that 316L and 317L like heat exchanger, acetic acid
plant, phosphoric acid plant, and bleaching equipment, etc. that
handle liquid including chlorine ion are not endured |
U321 |
SUS321 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
9.00`
13.00 |
17.00`
19.00 |
- |
- |
Ti
5~C
more |
The
one that Ti is added, and intergranular corrosion was improved.
It is not possible to recommend it to the decoration parts. |
U347 |
SUS347 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
9.00`
13.00 |
17.00`
19.00 |
- |
- |
Nb+Ta
10~C
more |
The
one that Nb is contained, and intergranular corrosion was improved.
|
UXM7 |
SUSXM7 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
8.50`
10.50 |
17.00`
19.00 |
- |
3.00`
4.00 |
- |
Steel
kind that adds Cu to 304, and attempts improvement of cold working.
For cold forging |
UXM15J1 |
SUSXM15J1 |
0.08
or less |
3.00`
5.00 |
2.00
or less |
0.040
or less |
0.0
under-30 |
11.50`
15.00 |
15.00`
20.00 |
- |
- |
- |
304
Ni is increased, Si is added, and stress corrosion cracking is improved.
For environment including chlorine ion |
U305J1 |
SUS305J1 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
11.00`
13.50 |
16.50`
19.00 |
- |
- |
- |
With
305 low carbon steels. Work hardening is low. 305 and the usage
are the same. |
U384 |
SUS384 |
0.08
or less |
1.00
or less |
2.00
or less |
0.040
or less |
0.0
under-30 |
17.00`
19.00 |
15.00`
19.00 |
- |
- |
- |
Wood
for cold forging and cold molding with which work hardening is low,
and severer than 305. |
High frequency
sign |
JIS
sign |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Cu |
Others |
Character
and usage |
Chemical
composition(%) |
- Mo 0.60%
or less can be added. |